907 Suhu Tinggi Novolac Resin Swancor 907 ChemPulse

907 Suhu Tinggi Novolac Resin Swancor 907 ChemPulse

$3≥1000Others

Jenis bayaran:	L/C,Western Union,T/T
Pesanan minimum:	1000 kilogram
Port:	Shanghai Port of China

Hubungi sekarang

Penerangan produk

Atribut Produk

Pembungkusan & Penghantaran

Penerangan produk

Atribut Produk

CAS No.: un-available

Other Names: VE resin

MF: un-available

EINECS No.: un-available

Type: Synthetic Resin And Plastics

Brand Name: Swancor

Model Number: 907

Appearance: Light yellow transparent liquid

Density: 1.06±0.02kg/L

Viscosity: 430±150 cps (LVT#3-60rpm/25℃)

Solid Content: 62±1.5%

Gel Time: 15-25min

Storage Period: 4 month(below 25℃)

Manufacturing Process: filament winding or spray up process

Feature: high distortion temperature

Application: high-temperature flue and smoke pipe

Delivery Time: 20 days after deposit in account

Place Of Origin: Jiangsu, China

Purity: 55%

Pembungkusan & Penghantaran

Unit Jualan	:	kilogram
Jenis Pakej	:	Dikemas dalam kotak plastik, 20kg/gendang
Contoh Gambar	:

Suhu tinggi novolac resin swancor 907 chempulse1



Penerangan produk

Penerangan Produk

Resin ester vinil epoksi novolac

1. Ciri -ciri mekanikal surperior dan rintangan kimia pada suhu tinggi.
2. Suhu penyimpangan haba yang tinggi
3. Dengan rintangan fatique yang sangat baik.
4. Sesuai untuk aplikasi yang lebih agresif.

5. Warna pemutus yang lebih rendah

Penampilan produk

Penampilan

Pakej 20kg/gendang

Harta benda pemutus resin poliester

Appearance	light yellow transparent liquid
Density	1.06±0.02kg/L
Viscosity	430±150 cps (LVT#3-60rpm/25℃)
Solid content	62±1.5%
Gel time	15-25min (55%MEKPO：1.2%，6% cobalt Octoate 0.4%，100%DMA：0.05%，temperature：25℃ water bath)
Storage period	4 month(below 25℃)

Lembaran data produk

Item	Data	Test method
Tensile strength	76-90MPa	ASTM D 638
Tensile modulus	3.4-3.7GPa	ASTM D 638
Elongation	2.5-4.0%	ASTM D 638
Bending strength	124-145MPa	ASTM D 790
Bending modulus	3.7-4.1GPa	ASTM D 638
Distortion temperature	144-150℃	ASTM D 638
Hardness	40-46 Barcol	ASTM D 2583

Permohonan

tangki penyimpanan asid hidroklorik (HCl)

Kimia: 31% HCl, suhu 60 ℃ Vinyl Resin Digunakan: Swancor Chempulse 907

Proses Pembuatan: Sembur lapisan

Permohonan Swancor 907

Produk siri Swancor 907 adalah resin ester vinil epoksi fenolik dengan ketumpatan silang yang tinggi dan rintangan haba yang baik (
Suhu herotan haba boleh mencapai 150 ℃ atau lebih tinggi), terutamanya untuk penyelesaian yang mengandungi klorin atau pelarut organik. Ia
boleh digunakan dalam beberapa keadaan di mana suhu agak tinggi, seperti penyediaan serabut suhu tinggi dan asap
paip, dan dalam industri chlor-alkali, industri pembuatan paperm, penyimpanan minyak dan gas, industri elektroplating, peleburan logam
Industri, dan lain -lain juga digunakan secara meluas.

Pakej