resin poliester gentian kaca thixotropic

$17001-19 Others

$1688≥20Others

Jenis bayaran:	T/T
Port:	Shanghai Port

Hubungi sekarang

Penerangan produk

Atribut Produk

Model No.: TC-K196

CAS No.: 25608-12-2

Other Names: unsaturated polyester resin for boat

MF: C3H5NO)n

EINECS No.: 208-750-2

Type: Synthetic Resin And Plastics

Brand Name: Fullmark

Model Number: TC-196, TC-196

Appearance: Light yellow transparent liquid

Pembungkusan: metal barrel

Penggunaan: unsaturated polyester resin for boat

Net Weight: 220kg

Sijil: Msds

Storage Period: 90 days .but it's 30 days if add thixotropice accelerator

Storage Condition: Below 25℃ in dark

Senarai Produk Berkaitan: unsaturated polyester resin for boat

Place Of Origin: Jiangsu, China

Purity: 61-67%

Jenama: Fullmark

Pembungkusan & Penghantaran

Unit Jualan	:	ton
Jenis Pakej	:	Barrel logam

The file is encrypted. Please fill in the following information to continue accessing it

FRP Boats Yachts Pra-Promoted Thixotropic Fiberglass Polyester Resin1



Penerangan produk

TC-K196 Penerangan Produk Polyester Tempatan

TC196 Tujuan Umum Polyester Resin tak tepu mempunyai ciri -ciri gentian kaca yang baik, rintangan UV yang baik dan kekuatan mekanikal.

TC-K196 Unsaturated polyester resin

Sifat resin poliester tak tepu cecair

Item	Unit	Measured data	Testing method
Appearance	-	Light yellow transparent liquid	GB-T 8237.4.1.1
viscosity	25℃,Pa·s	0.25-0.45	GB/T 7193.1
Gel time	25℃,min	9-17	GB/T 7193.6
Acid value	mgKOH/g	28-36	GB/T 2895
Solid content	%	61-67	GB/T 7193.3

Masa gel: 50% sikloheksanon peroksida: 4%; Pemecut E1: 4%;

Harta benda pemutus resin

Item	Measured data	Unit	Testing method
Barcol hardness	46	—	GB 3854-83
Distortion temperature	66	℃	GB 1634-04
Elongation at break	1.8	%	GB 2568-95
Notes:1)casting body sample preparation method according to GB 8237-87,curing system:hardener 55%MEKPO:2%,promoter E1; 2)post cure system:60℃×2h+80℃×2h.

FRP PROPERATIK FIZIKAL

Item	Unit	Measured data	Testing method
Bending strength	MPa	325	GB/T2570-95
Bending modulus	MPa	1.40×104	GB/T2570-95
Notes:1)casting body sample preparation method according to GB 8237-87,curing system:hardener 55%MEKPO:2%,promoter E1; 2)post cure system:60℃×3h+110℃×3h.