Klasifikasi: Ejen tambahan kimia
CAS No.: 614-45-9, 614-45-9
Other Names: TBPB
MF: C3h5no)n
Type: SMC BMC process catalyst
Penggunaan: Plastic Auxiliary Agents, unsaturated polyester resin catalyst
Brand Name: SYRGIS
Model Number: NOROX KP-925H
Appearance: Yellowish Liquid
Peroxide Content: Ca. 99 % w/w
Active Oxygen: Ca. 8.16 % w/w
De-sensitising Agent: none
Density At 20°C: Ca. 1.04 g/cm3
Viscosity At 20°C: Ca. 8 mPa.s
Refractive Index At 20°C: Ca. 1.499
Miscibility: Immiscible with water, soluble in alcohols, phthalates
Critical Temperature (SADT): Ca. 60°C
Purity: 100%
Place Of Origin: Jiangsu, China
| Unit Jualan | : | kilogram |
| Jenis Pakej | : | Barel plastik |
| Contoh Gambar | : |
|
The file is encrypted. Please fill in the following information to continue accessing it
NOROX ® TBPB
Tert.butylperoxybenzoate CAS#614-45-9
Cecair, teknikal tulen
Penerangan
Cecair mudah alih, mudah alih, yang terdiri daripada benzoat TERT.Butylperoxy secara teknikal. Perester aromatik ini digunakan sebagai pemula (sumber radikal) dalam pengawetan resin poliester tak tepu. Permohonan utama: Pencetakan akhbar panas SMC atau BMC pada 130-160 ° C.
Ini produk adalah dalam pematuhan dengan The Elektrog (EU-direktif: ROHS 2002/95/misalnya, WEEE 2002/96/contohnya)
Data separuh hayat
10h / 1h / 1min (0.1 m / benzena): 104 ° C / 124 ° C / 165 ° C
Menyembuhkan poliester:
Menyembuhkan ejen untuk Naik resin. Sesuai untuk semua Resin jenis. Suhu Julat: 130- 160 ° C. Penggunaan Tahap: 1-2% sebagai dibekalkan. "Shelf hidup " (Gel masa dari Resin + peroksida) beberapa bulan pada suhu ambien, bergantung kepada jenis resin. Sensitif terhadap beberapa pengisi dan pigmen serta garam kobalt atau tertiari amina aromatik. Kehidupan rak dapat berlanjutan dengan menambah 0.1-0.3% Inhibitor SM 500.
Ciri -ciri pengawetan:
Dalam lingkungan 85-95 ° C (suhu "kick-off") kadar pengawetan tidak begitu tinggi, kecuali terdapat tindak balas tindak balas (contohnya dalam acuan penahan haba). Masa penyembuhan yang benar-benar pendek 1-3 minit boleh dicapai hanya melebihi 120 ° C. Oleh itu, julat suhu optimum untuk pencetakan akhbar panas ialah 130- 160 ° C.
Kaedah Pemprosesan:
Terutamanya mencetak akhbar panas sebatian cetakan lembaran (SMC) atau sebatian cetakan pukal (BMC), serta impregnasi, mencelupkan lilitan dawai.
Aktiviti
Pengaruh suhu dan dos peroksida 1 untuk menyembuhkan prestasi dan tahap penyembuhan. Pencetakan akhbar panas 16 mm pelet SMC tebal dan lembaran SMC tebal 3 mm.
|
Temperature of mould |
130°C |
130°C |
140°C |
140°C |
150°C |
150°C |
160°C |
160°C |
|
Formulation (parts of weight) |
|
|
|
|
|
|
|
|
|
Standard SMC (resin proportion) |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
|
Norox® TBPB |
1 |
2 |
1 |
2 |
1 |
2 |
1 |
2 |
|
Curing performance (SMC pellets) |
|
|
|
|
|
|
|
|
|
Flow time (min) |
1.50 |
1.35 |
1.15 |
1.00 |
0.95 |
0.80 |
0.75 |
0.70 |
|
Time to peak tmax (min) |
2.70 |
2.40 |
1.90 |
1.60 |
1.40 |
1.30 |
1.20 |
- |
|
Peak exotherm Tmax (°C) |
171 |
170 |
174 |
174 |
178 |
178 |
185 |
183 |
|
Degree of cure (SMC sheets2) |
|
|
|
|
|
|
|
|
|
Barcol (934) hardness |
20 |
20 |
25 |
25 |
30 |
30 |
30 |
30 |
|
Residual styrene content (%) |
2.6 |
1.7 |
0.8 |
0.6 |
0.5 |
0.2 |
<0.1 |
<0.1 |
1 ) The jumlah ditambah adalah bersamaan ke 1% atau 2% w/w teknik. Murni t-butil perce-perconzoate
2 ) Kitaran akhbar untuk lembaran SMC adalah sama dengan Tmax. daripada pelet SMC yang sepadan.
Maklumat lanjut mengenai ejen pengawetan yang sesuai untuk resin poliester tak tepu diberikan dalam risalah permohonan kami mengenai subjek ini.
Pembungkusan
Pembungkusan standard Norox TBPB adalah 25 kg.
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Contact Now