TM-2001 Produk FRP Air Resin Poliester Tanpa tepu

TM-2001 Produk FRP Air Resin Poliester Tanpa tepu

$1700≥1Others

Jenis bayaran:	T/T
Pesanan minimum:	1 ton
Port:	Shanghai Port

Option:

220Kg

Hubungi sekarang

Penerangan produk

Atribut Produk

Pembungkusan & Penghantaran

Penerangan produk

Atribut Produk

Model No.: TM-2001

Jenama: TC

CAS No.: 25608-12-2

Other Names: unsaturated polyester resin for boat

MF: C3H5NO)n

EINECS No.: 208-750-2

Type: Synthetic Resin And Plastics

Brand Name: Fullmark

Model Number: TC-196, TC-196

Appearance: Light yellow transparent liquid

Pembungkusan: metal barrel

Penggunaan: unsaturated polyester resin for boat

Net Weight: 220kg

Sijil: Msds

Storage Period: 90 days .but it's 30 days if add thixotropice accelerator

Storage Condition: Below 25℃ in dark

Senarai Produk Berkaitan: unsaturated polyester resin for boat

Place Of Origin: Jiangsu, China

Purity: 61-67%

Jenama: Fullmark

Pembungkusan & Penghantaran

Unit Jualan	:	ton
Jenis Pakej	:	Barrel logam
Contoh Gambar	:

The file is encrypted. Please fill in the following information to continue accessing it

Kapal, bot dan produk FRP air lain tidak tepu resin1



Penerangan produk

Penerangan Produk

TC-K196 resin poliester tak tepu

Penerangan Produk

TC196 Tujuan Umum Resin Poliester Tidak tepu mempunyai Impregnation Fiberglass yang Baik, Rintangan UV yang Baik dan Kekuatan Mekanikal.

Sifat resin poliester tak tepu cecair

Item	Unit	Measured data	Testing method
Appearance	-	Light yellow transparent liquid	GB-T 8237.4.1.1
viscosity	25℃,Pa·s	0.25-0.45	GB/T 7193.1
Gel time	25℃,min	9-17	GB/T 7193.6
Acid value	mgKOH/g	28-36	GB/T 2895
Solid content	%	61-67	GB/T 7193.3

Masa Gel: 50% Cyclohexanone Peroksida: 4%; Accelerator E1: 4%;

Harta benda pemutus resin

Item	Measured data	Unit	Testing method
Barcol hardness	46	—	GB 3854-83
Distortion temperature	66	℃	GB 1634-04
Elongation at break	1.8	%	GB 2568-95
Notes:1)casting body sample preparation method according to GB 8237-87,curing system:hardener 55%MEKPO:2%,promoter E1; 2)post cure system:60℃×2h+80℃×2h.

Harta fizikal FRP

Item	Unit	Measured data	Testing method
Bending strength	MPa	325	GB/T2570-95
Bending modulus	MPa	1.40×104	GB/T2570-95
Notes:1)casting body sample preparation method according to GB 8237-87,curing system:hardener 55%MEKPO:2%,promoter E1; 2)post cure system:60℃×3h+110℃×3h.

Pakej resin dan keadaan penyimpanan

P edik dalam laras logam, 220kg/barel (kira -kira 55 gelen)
Cuba untuk mengelakkan resin cecair dari cahaya matahari dan sumber haba secara langsung
F lammable, harus menjauhkan diri dari api terbuka
S Helf Life adalah 3 bulan di bawah 25 ℃
Simpan dan beroperasi di tempat yang kering dan berventilasi