Bahan resin poliester tak tepu untuk skylight

Bahan resin poliester tak tepu untuk skylight

$2500≥1Others

Jenis bayaran:	T/T
Pesanan minimum:	1 ton
Port:	Shanghai port

Hubungi sekarang

Penerangan produk

Atribut Produk

Pembungkusan & Penghantaran

Penerangan produk

Atribut Produk

CAS No.: 25608-12-2

Other Names: unsaturated polyester resin

MF: C3H5NO)n

EINECS No.: 208-750-2

Type: Synthetic Resin And Plastics

Brand Name: TIANMA

Model Number: TM-108, TM-108

Appearance: transparent light yellow liquid

Pembungkusan: 220kg/barrel

Penggunaan: unsaturated polyester resin for skylight

Viscosity: 0.25~0.55 25℃,Pa.S

Gel Time: 30~60 25℃,min

Acid Value: 20~29 mgKOH/g

Solid Content: 62~69%

Storage Life: 3 month under 25℃

Senarai Produk Berkaitan: unsaturated polyester resin for skylight

Place Of Origin: Jiangsu, China

Purity: 66-72

Pembungkusan & Penghantaran

Unit Jualan

ton

The file is encrypted. Please fill in the following information to continue accessing it

Penerangan produk

TM-108 UP Resin Huraian Produk

TM-108 Aktif Retardant Retardant Resin UP adalah bahan komposit resin poliester tak tepu khas untuk skylight. Unsur -unsur retardan yang berkaitan secara langsung dengan rantaian utama resin, mengatasi pengurangan harta mekanikal dan kesalahan pengurangan harta retardan api yang disebabkan oleh migrasi TBPA dan TBPA yang ditambah.

TM- 10 8 Reaktif Retardant Retardant Resin Up mempunyai kelikatan yang rendah, impregnasi yang baik dengan gentian kaca, sesuai untuk proses gentian kaca " e " Topeng Perlombongan , Skylight Plane .

harta resin cecair :

item	unit	standard	testing method
appearance	——	transparent light yellow liquid	GB/T 8237.4.1.1
viscosity	25℃,Pa.S	0.25~0.55	GB/T 7193.1
gel time	25℃,min	30~60	GB/T 7193.6
acid value	mgKOH/g	20~29	GB/T 2895
solid content	%	62~69	GB/T 7193.3
Refraction	nD25	1.5150~1.5220	GB 8238

Masa Gel: 50% Cyclohexanone Peroksida Paste: 4% Accelerator E1: 4%.

Harta Produk FRP ( untuk rujukan )

item	unit	measured data	testing method
bending strength	MPa	348	GB/T2570—95
LOI	%	32	GB/T 2406—93
tensile strength	MPa	288	GB/T2568-95
Impact toughness	KJ/m2	252	GB/T2571-95
Light transmission	%	75-80	ZB Q23001-81

Nota:

1. Kaedah penyediaan sampel FRP sesuai dengan GB 8237-87 .

2. Sistem Curing: Ejen pengawetan 55% MEKPO : 2% , Ejen pengawetan E1 : 2% .

3. Penyembuhan Post: 25 ℃ Suhu bilik 21 hari.

4. FRP Ujian Transmisi Cahaya: 4 Lapisan 0.21 711 Alkali Woven Roving.

Resipi ( untuk rujukan )

Item	Parts by weight
TM-108 UP resin	100
Curing agent55%MEKPO	2
Accelerator E5 (colorless)	1-4 (according to local temperature)

Nota:

a. TM108 Resin Gel Time Long, jadi sila gunakan E5 yang tidak berwarna E5, untuk mencapai produk siap warna cahaya.

b. Resin ini digunakan dengan roving tenunan alkali, tangan meletakkan produk siap mesti diletakkan di bawah suhu bilik selama 3 minggu sebelum berlepas dari kilang.

Penyimpanan

Disimpan di bawah 25 ℃ tempat perlindungan , api dan haba terpencil, jangka hayat 3 bulan.

Pembungkusan & Penghantaran